Title: Estudo de compósitos de partículas de madeira e PEBD reciclado na presença de agentes compatibilizantes
Other Titles: The Study of wood particules and recycled LDPE composites in the presence of coupling agents
???metadata.dc.creator???: Redighieri, Karla Isabel 
???metadata.dc.contributor.advisor1???: Costa, Dilma Alves
???metadata.dc.description.resumo???: Esta dissertação teve por objetivo utilizar o polietileno de baixa densidade reciclado (PEBDrec) como matriz termoplástica para obtenção de compósitos com partículas de madeira (PM) de eucalipto. A compatibilização desses compósitos foi realizada com lignina, sob a forma de lignossulfonato de amônio, e polietileno de alta densidade graftizado com anidrido (PE-g-MA). A razão PM/PEBDrec foi variada de modo a obter composições de 40/60, 50/50 e 60/40 %p/p. As partículas de madeira utilizadas na confecção desses compósitos foram tratadas com 5 e 10%, em massa de agente compatibilizante (lignina ou PE-g-MA). De modo a avaliar a eficiência desses compostos usados como agentes compatibilizantes, os resultados obtidos com esses materiais foram comparados com os resultados dos compósitos de partículas de madeira não-tratadas, de acordo com cada tipo de agente compatibilizante. O comportamento mecânico dos compósitos foi determinado a partir dos ensaios de tração e flexão, seguindo as normas ASTM D 638-03 e ASTM D 790-03, respectivamente. Pode-se concluir que os compósitos compatibilizados com PE-g-MA apresentaram uma melhoria nas propriedades mecânicas e na absorção de água, quando comparados com os compósitos com partículas de madeira tratadas com lignina e não-tratadas. Através da análise de ressonância magnética nuclear, foi possível observar que o aumento do teor das partículas acarretou em uma maior mobilidade das cadeias moleculares desses materiais.
Abstract: The objective of this work was to employ the recycled low density polyethylene as polymeric matrix with wood particles (PM) of eucalypt to obtain composites, in presence of lignin, from residue paper industry, as coupling agent. Besider lignin, PE-g-MA (functionalized polyethylene with maleic anhydride) was also used as coupling agent in order compare the efficiency. Three different compounds were prepared: 40/60, 50/50 e 60/40 (PM/LDPErec). The wood particles were treated with 5 e 10% in mass of coupling agent (lignin or PE-g-MA). To evaluate the efficiency of these coupling agents, the results obtained were compared with composites with untreated wood particles. The mechanical properties were characterized by tensile tests according to ASTM D-638-03 and flexural tests according to ASTM 790-03. Composites with wood particles treated with PE-g-MA ca be improvement in mechanical properties and wettability, whilst the lignin and untreated particles. By 1H NMR in solid state, it was observed that the mobility chains molecular decreased with an increase of wood particles content.
Keywords: modificação química
propriedades mecânicas
absorção de água
chemical modification
mechanical properties
water absorption
???metadata.dc.subject.cnpq???: Engenharia Química
Language: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade Federal Rural do Rio de Janeiro
???metadata.dc.publisher.initials???: UFRRJ
???metadata.dc.publisher.department???: Instituto de Tecnologia
???metadata.dc.publisher.program???: Curso de Pós-Graduação em Engenharia Química
Citation: REDIGHIERI, Karla Isabel. Estudo de compósitos de partículas de madeira e PEBD reciclado na presença de agentes compatibilizantes. 2006. 84 f. Dissertação (Mestrado em Engenharia Química). Instituto de Tecnologia, Universidade Federal Rural do Rio de Janeiro, Seropédica, RJ, 2006.
???metadata.dc.rights???: Acesso Aberto
URI: https://tede.ufrrj.br/jspui/handle/tede/344
Issue Date: 21-Feb-2006
Appears in Collections:MESTRADO EM ENGENHARIA QUÍMICA

Files in This Item:
File Description SizeFormat 
2006-Karla Isabel Redighieri.pdf5.43 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.